I did say use sand. I couldn't tell from your photo if there was sand in the mix. So many variables but I would certainly think that uneven heat would be bad. Have you looked at the coefficient of thermal expansion between the plaster and the PLA? If the PLA is considerably higher, I would think the solution would be a larger mold to increase the thickness of the plaster.